硅酸鋯珠(CZS):
     采用電解液中滴定成型，高溫?zé)Y(jié)定相的先進(jìn)工藝制成。珠內(nèi)由致密的硅酸鋯微粒組成微觀結(jié)構(gòu)，拒絕了毛隙和空腔，避免了晶相和玻璃相的分離，比同類珠子有更大的密度和硬度，磨耗率是同類硅酸鋯珠的1/2。中等的密度和硬度適合中低粘度漿料的分散和研磨，可匹配**部分的砂磨機(jī)，為通用型磨介。
氧化鋯含量: 64%,           氧化硅含量: 33%,
比      重: >4.0kg/dm³,    散      重: >2.5kg/L,
莫 氏 硬度: >7.0,          維 氏 硬度: >900kg/mm², 
耐 壓 強(qiáng)度: 1200N(2mm),    粒      徑: 0.4-3.2mm,
噸  磨  耗: 0.05kg/噸,     包      裝: 25kg/桶
CZS zirconium silicate beads are shaped in electrolyte solution and hardened at a high temperature in kilin. Compared to the other zircon beads and the ATZ beads, they have homogenous microstructure and no air pockets. This give them 1/2 lower beads wear than the others. The middle density and high crushing strength features are suitable to grinding slurry in visicosity from low to middle in more kinf of beads mills.
ZrO₂ %: 64 ,                   SiO2 %: 33
Density: >4.0kg/dm³,            Bulk Density: 2.56kg/L
Hardness Vickers: >900kg/mm²,  Crushing Strength: 1200N (2mm), 
Sizes: 0.4-5.5mm ,             Packing: 25kg/bucket